Failure Analysis of Spherical Roller Bearing

JULIŠ, M. ČELKO, L. SPOTZ, Z. DOLEŽAL, P. PAVLOUŠKOVÁ, Z. ŠVEJCAR, J.

Original Title

Failure Analysis of Spherical Roller Bearing

English Title

Failure Analysis of Spherical Roller Bearing

Type

conference paper

Language

en

Original Abstract

The failure of a spherical-roller bearing consisting of spherical rollers, outer and inner rings made of 100CrMn6 steel was studied. After a trial test, in which several spherical rollers were completely destroyed and a long continuous radial crack appeared in the outer ring, pitting degradation was observed on all bearing parts. The bearing components were studied (separately) by means of light and electron microscopy. The chemical composition was estimated by means of glow discharge optical emission spectroscopy. X-ray diffraction was utilized for qualitative and quantitative phase analyses. As a representative of mechanical properties, the hardness was also measured.

English abstract

The failure of a spherical-roller bearing consisting of spherical rollers, outer and inner rings made of 100CrMn6 steel was studied. After a trial test, in which several spherical rollers were completely destroyed and a long continuous radial crack appeared in the outer ring, pitting degradation was observed on all bearing parts. The bearing components were studied (separately) by means of light and electron microscopy. The chemical composition was estimated by means of glow discharge optical emission spectroscopy. X-ray diffraction was utilized for qualitative and quantitative phase analyses. As a representative of mechanical properties, the hardness was also measured.

Keywords

Spherical roller bearings; Pitting; Light and electron microscopy; X-ray diffraction

RIV year

2014

Released

01.04.2014

Publisher

Trans Tech Publication

Location

Switzerland

ISBN

978-3-03835-072-9

Book

Metallography XV

Pages from

247

Pages to

250

Pages count

4

URL

BibTex


@inproceedings{BUT106856,
  author="Martin {Juliš} and Ladislav {Čelko} and Zdeněk {Spotz} and Pavel {Doležal} and Zina {Pavloušková} and Jiří {Švejcar}",
  title="Failure Analysis of Spherical Roller Bearing",
  annote="The failure of a spherical-roller bearing consisting of spherical rollers, outer and inner rings made of 100CrMn6 steel was studied. After a trial test, in which several spherical rollers were completely destroyed and a long continuous radial crack appeared in the outer ring, pitting degradation was observed on all bearing parts. The bearing components were studied (separately) by means of light and electron microscopy. The chemical composition was estimated by means of glow discharge optical emission spectroscopy. X-ray diffraction was utilized for qualitative and quantitative phase analyses. As a representative of mechanical properties, the hardness was also measured.",
  address="Trans Tech Publication",
  booktitle="Metallography XV",
  chapter="106856",
  doi="10.4028/www.scientific.net/MSF.782.247",
  howpublished="print",
  institution="Trans Tech Publication",
  number="782",
  year="2014",
  month="april",
  pages="247--250",
  publisher="Trans Tech Publication",
  type="conference paper"
}