Originální abstrakt

Electrophoretic deposition of Al2O3 and ZrO2 powders from isopropanol suspension in the presence of monochloroacetic acid under constant-current conditions was studied. The deposits were prepared under different electrical conditions of deposition. It was found that the deposits prepared at low current densities (500 microA) contained smaller pores and achieved higher green densities than deposits prepared at high current densities (20 mA). The deposits prepared at low current densities were formed just by part of the particles in the suspension because of decreasing of efficiency of electrophoretic deposition process.

Anglický abstrakt

Electrophoretic deposition of Al2O3 and ZrO2 powders from isopropanol suspension in the presence of monochloroacetic acid under constant-current conditions was studied. The deposits were prepared under different electrical conditions of deposition. It was found that the deposits prepared at low current densities (500 microA) contained smaller pores and achieved higher green densities than deposits prepared at high current densities (20 mA). The deposits prepared at low current densities were formed just by part of the particles in the suspension because of decreasing of efficiency of electrophoretic deposition process.

BibTex


@article{BUT92721,
  author="Hynek {Hadraba} and Daniel {Drdlík} and Zdeněk {Chlup} and Karel {Maca} and Ivo {Dlouhý}",
  title="Control of Electrophoretic Deposition Kinetics for Preparation of Laminated Alumina/Zirconia Ceramic Composites",
  annote="Electrophoretic deposition of Al2O3 and ZrO2 powders from isopropanol suspension in the presence of monochloroacetic acid under constant-current conditions was studied. The deposits
were prepared under different electrical conditions of deposition. It was found that the deposits
prepared at low current densities (500 microA) contained smaller pores and achieved higher green
densities than deposits prepared at high current densities (20 mA). The deposits prepared at low
current densities were formed just by part of the particles in the suspension because of decreasing of
efficiency of electrophoretic deposition process.",