Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys

MACA, K., CIHLÁŘ, J.

Originální název

Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys

Anglický název

Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys

Jazyk

en

Originální abstrakt

The structure of interaction interface after contact of molten nickel alloys Ni20Cr and Ni20Cr5Ti with the single crystal alumina of defined orientation at the temperature range from 1773K to 1973K for 8 and 16 hours and under pressure of argon atmosphere 0.12MPa was investigated by means of SEM, microananlysis and XRD analysis.

Anglický abstrakt

The structure of interaction interface after contact of molten nickel alloys Ni20Cr and Ni20Cr5Ti with the single crystal alumina of defined orientation at the temperature range from 1773K to 1973K for 8 and 16 hours and under pressure of argon atmosphere 0.12MPa was investigated by means of SEM, microananlysis and XRD analysis.

Dokumenty

BibTex


@inbook{BUT51736,
  author="Karel {Maca} and Jaroslav {Cihlář}",
  title="Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys",
  annote="The structure of interaction interface after contact of molten nickel alloys Ni20Cr and Ni20Cr5Ti with the single crystal alumina of defined orientation at the temperature range from 1773K to 1973K for 8 and 16 hours and under pressure of argon atmosphere 0.12MPa was investigated by means of SEM, microananlysis and XRD analysis.",
  address="The Federation of European Materials Societies",
  booktitle="Junior Euromat 94",
  chapter="51736",
  institution="The Federation of European Materials Societies",
  year="1994",
  month="january",
  pages="9",
  publisher="The Federation of European Materials Societies",
  type="book chapter"
}