Originální abstrakt

The structure of alumina cores after interaction with nickel alloys (Ni-Cr, Ni-CrTi, Ni-CrAl) at temperatures from 1773 to 1973 K for periods from 90min to 2h at argon atmosphere pressures of 0.4Pa and 0.12MPa was studied by means of SEM, microanalysis and XRD analysis.

Anglický abstrakt

The structure of alumina cores after interaction with nickel alloys (Ni-Cr, Ni-CrTi, Ni-CrAl) at temperatures from 1773 to 1973 K for periods from 90min to 2h at argon atmosphere pressures of 0.4Pa and 0.12MPa was studied by means of SEM, microanalysis and XRD analysis.

Dokumenty

BibTex


@inbook{BUT51728,
  author="Karel {Maca} and Jaroslav {Cihlář}",
  title="Alumina Shell Moulds and Cores for Directional Solidification of Ni-alloys",
  annote="The structure of alumina cores after interaction with nickel alloys (Ni-Cr, Ni-CrTi, Ni-CrAl) at temperatures from 1773 to 1973 K for periods from 90min to 2h at argon atmosphere pressures of 0.4Pa and 0.12MPa was studied by means of SEM, microanalysis and XRD analysis.",
  address="International Ceramics Federation",
  booktitle="Alumina Shell Moulds and Cores for Directional Solidificatio",
  chapter="51728",
  institution="International Ceramics Federation",
  year="1995",
  month="january",
  pages="2839",
  publisher="International Ceramics Federation",
  type="book chapter"
}