Analysis of surface defects of aluminium components with hard anodized layers

KLAKURKOVÁ, L. JULIŠ, M. ČELKO, L. HORYNOVÁ, M. HÉGR, E. ŠVEJCAR, J.

Originální název

Analysis of surface defects of aluminium components with hard anodized layers

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

Final quality inspection regularly reveals surface defects on components after hard anodizing. The aim of the analysis was to identify the cause of the defects and unambiguously determine whether the defect is caused by the quality of the base material, manufacturing technology of the component, the heat treatment or by the final surface treatment technology (anodizing). Analysis of the chemical composition and hardness measurements were performed to eliminate the possibility of any errors during material selection and heat treatment process. The capillary test revealed two major defects and also small amount of minor defects. To determine cause of the defects, light and scanning electron microscopy including EDS chemical microanalysis was used. Detailed study of the major defect and EDS microanalysis of its interior confirmed existence of defect prior to coating formation. Further examination of the major defect and its surroundings led to conclusion, that the defect was formed during primary foundry processes when billet was manufactured.

Klíčová slova

Failure analysis; Hard anodizing; Rolling defects; Metallurgical investigation; Metallography

Autoři

KLAKURKOVÁ, L.; JULIŠ, M.; ČELKO, L.; HORYNOVÁ, M.; HÉGR, E.; ŠVEJCAR, J.

Rok RIV

2015

Vydáno

1. 10. 2015

Nakladatel

Elsevier

Místo

Elsevier

ISSN

1350-6307

Periodikum

ENGINEERING FAILURE ANALYSIS

Ročník

56

Číslo

1

Stát

Spojené království Velké Británie a Severního Irska

Strany od

300

Strany do

306

Strany počet

7

URL

http://dx.doi.org/10.1016/j.engfailanal.2015.01.013

BibTex

@article{BUT116567,
  author="Lenka {Klakurková} and Martin {Juliš} and Ladislav {Čelko} and Miroslava {Horynová} and Eduard {Hégr} and Jiří {Švejcar}",
  title="Analysis of surface defects of aluminium components with hard anodized layers",
  journal="ENGINEERING FAILURE ANALYSIS",
  year="2015",
  volume="56",
  number="1",
  pages="300--306",
  doi="10.1016/j.engfailanal.2015.01.013",
  issn="1350-6307",
  url="http://dx.doi.org/10.1016/j.engfailanal.2015.01.013"
}