Sodium Hexametaphosphate as Deflocculation Agent for Calcium Aluminate Cements in Porcelain Body

SOKOLÁŘ, R. VODOVÁ, L.

Originální název

Sodium Hexametaphosphate as Deflocculation Agent for Calcium Aluminate Cements in Porcelain Body

Anglický název

Sodium Hexametaphosphate as Deflocculation Agent for Calcium Aluminate Cements in Porcelain Body

Jazyk

en

Originální abstrakt

Influence of typical ceramic deflocculant – sodium hexametaphosphate – on the rheological properties (viscosity) of calcium aluminate cement paste, porcelain raw materials mixture (casting slip), and fired porcelain body respectively, was determined. It was used two different typed of calcium aluminate cements (from two sources – producers - Istra, Almatis) with different content of Al2O3 (40 % and 70 %). Sodium hexametaphosphate decreases of water content needed to prepare slip casting with constant viscosity. Deflocculant increases the modulus of rupture MOR of dried green body and its bulk density. Sodium hexametaphosphate admixture is very suitable for the creation of porcelain body with low porosity after firing.

Anglický abstrakt

Influence of typical ceramic deflocculant – sodium hexametaphosphate – on the rheological properties (viscosity) of calcium aluminate cement paste, porcelain raw materials mixture (casting slip), and fired porcelain body respectively, was determined. It was used two different typed of calcium aluminate cements (from two sources – producers - Istra, Almatis) with different content of Al2O3 (40 % and 70 %). Sodium hexametaphosphate decreases of water content needed to prepare slip casting with constant viscosity. Deflocculant increases the modulus of rupture MOR of dried green body and its bulk density. Sodium hexametaphosphate admixture is very suitable for the creation of porcelain body with low porosity after firing.

Dokumenty

BibTex


@inproceedings{BUT106915,
  author="Radomír {Sokolář} and Lucie {Keršnerová}",
  title="Sodium Hexametaphosphate as Deflocculation Agent for Calcium Aluminate Cements in Porcelain Body",
  annote="Influence of typical ceramic deflocculant – sodium hexametaphosphate – on the rheological properties (viscosity) of calcium aluminate cement paste, porcelain raw materials mixture (casting slip), and fired porcelain body respectively, was determined. It was used two different typed of calcium aluminate cements (from two sources – producers - Istra, Almatis) with different content of Al2O3 (40 % and 70 %). Sodium hexametaphosphate decreases of water content needed to prepare slip casting with constant viscosity. Deflocculant increases the modulus of rupture MOR of dried green body and its bulk density. Sodium hexametaphosphate admixture is very suitable for the creation of porcelain body with low porosity after firing.",
  booktitle="Advanced Materials Research. Binders and Materials XI. Chapter 1: Cement and Binders Based on Cement",
  chapter="106915",
  doi="10.4028/www.scientific.net/AMR.897.30",
  howpublished="online",
  number="1",
  year="2014",
  month="february",
  pages="30--33",
  type="conference paper"
}