Reconstruction of fracture process zone during tensile failure of quasi-brittle materials

článek v časopise - ostatní, Jost

angličtina

The paper outlines a technique for estimation of the size and shape of an inelastic zone evolving around a crack tip during the tensile failure of structures/structural members made of quasi-brittle building materials, particularly cementitious composites. The technique is based on an amalgamation of several concepts dealing with the failure of structural materials, i.e. multi-parameter linear elastic fracture mechanics, classical non-linear fracture models for concrete (equivalent elastic crack and cohesive crack models), and the plasticity approach. The benefit of this technique is expected to be seen in the field of the determination of fracture characteristics describing the tensile failure of quasi-brittle silicate-based composites. The method is demonstrated using an example of a (numerically simulated) fracture test involving the three-point bending of a notched beam and validated by experimentally obtained results of three-point bending and wedge-splitting tests taken from the literature.

cementitious composites, fracture, quasi-brittle, fracture process zone, multi-parameter linear elastic fracture mechanics, effective crack model, cohesive crack model, Rankine strength criterion.

VESELÝ, V.; FRANTÍK, P.

2010

1. 10. 2010

Plzeň, Česká republika

1802-680X

Applied andComputational Mechanics

4

2

Česká republika

237

250

14