Detail publikace

Selfordered Hexagonal Pore Structure of Anodized Alumina Depposited on Si Substrate

HRDÝ, R., HUBÁLEK, J.

Originální název

Selfordered Hexagonal Pore Structure of Anodized Alumina Depposited on Si Substrate

Anglický název

Selfordered Hexagonal Pore Structure of Anodized Alumina Depposited on Si Substrate

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

čeština

Originální abstrakt

The main idea of this work is to prepare self ordered hexagonal pore structure anodization of aluminum layer. Anodized alumina is used as a mask for deposition of ordered nanowires or nanotubes. Diameters of pores are 20-80 nm depending on used electrolyte. The interpore distances are between 20-120 nm. Fabrication of anodized alumina is not simple process. Many factors affect successful preparation of ordered structure like the temperature, crystal structure of aluminum film and the concentration of used solution.

Anglický abstrakt

Hlavní myšlenka je vytvoření samouspořádané oxidové porézní masky na tenké hliníkové vrstvě.

Klíčová slova v angličtině

Sensors, Anodized Alumina, Nanoparticles

Autoři

HRDÝ, R., HUBÁLEK, J.

Rok RIV

2006

Vydáno

19. 4. 2006

Nakladatel

Ing. Zdeněk Novotný CSc, Ondráčkova 105, Brno

Místo

Brno, Česká Republika

ISBN

80-214-3161-X

Kniha

Proceedings of the 12. Conference STUDENT EEICT 2006, Volume 2

Číslo edice

1

Strany od

130

Strany do

132

Strany počet

3

BibTex

@inproceedings{BUT20129,
  author="Radim {Hrdý} and Jaromír {Hubálek}",
  title="Selfordered Hexagonal Pore Structure of Anodized Alumina Depposited on Si Substrate",
  booktitle="Proceedings of the 12. Conference STUDENT EEICT 2006, Volume 2",
  year="2006",
  number="1",
  pages="3",
  publisher="Ing. Zdeněk Novotný CSc, Ondráčkova 105, Brno",
  address="Brno, Česká Republika",
  isbn="80-214-3161-X"
}