Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma

ŘÁDKOVÁ, L. FOJTÍKOVÁ, P. SÁZAVSKÁ, V. KRČMA, F.

Originální název

Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma

Anglický název

Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma

Jazyk

en

Originální abstrakt

Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy.

Anglický abstrakt

Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy.

Dokumenty

BibTex


@misc{BUT101827,
  author="Lucie {Řádková} and Petra {Miková} and Věra {Sázavská} and František {Krčma}",
  title="Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma",
  annote="Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy.",
  booktitle="EUROCORR 2013 - Book of Abstracts",
  chapter="101827",
  howpublished="print",
  year="2013",
  month="september",
  pages="1317--1317",
  type="abstract"
}