Effect of Plasmachemical Treatment on Corrosion Layers of Iron

MAZÁNKOVÁ, V. SÁZAVSKÁ, V. KRČMA, F.

Originální název

Effect of Plasmachemical Treatment on Corrosion Layers of Iron

Typ

různé

Jazyk

angličtina

Originální abstrakt

Application of plasmas is a new way of effective and fast treatment leading to conservation of metallic corroded objects. Removal of corrosion products is based on plasmachemical reduction of corrosion layers by radio-frequency (RF) low pressure hydrogen plasma. Influence of this process on corroded iron samples was investigated. OH radicals formed during this process were measured by optical emission spectroscopy; simultaneously, sample temperature was measured by a thermocouple placed inside the objects. The value of OH radical integral intensity represented quantitative ablation of oxygen from a corrosion layer. Sample temperature was an important indicator of sample protection against metallographic changes. It was proved that both hydrogen atom reduction and thermal decomposition were employed in the removal process. The XRD and SEM/EDX analyses of corroded and treated samples were done.

Klíčová slova

model corrosion layers of iron samples, low-pressure low-temperature hydrogen plasma, plasma chemical reduction of corrosion layers

Autoři

MAZÁNKOVÁ, V.; SÁZAVSKÁ, V.; KRČMA, F.

Vydáno

14. 7. 2013

Místo

Granada

Strany od

PS3-091

Strany do

PS3-091

Strany počet

4